• Finish: Ceramic-like with over 50% ceramic content, no extra post-thermal treatment needed.
• Stiffness: High E modulus of 5800 MPa, strong wear resistance, low water absorption.
• Fluidity: Ultra-low viscosity at 120 mPas, high-speed printing, easy post-processing.
• Heat Resistance: Enhanced performance after thermal treatment at 80°C for 24 hours.

SDS

User Guide

• Viscosity: 120 cP
• Density: 1.45 g/cm3
• Surface Hardness: >90 Shore D
• Tensile Modulus: 5800 MPa
• Tensile Stress at Break: 62 MPa
• Flexural Modulus: 5400 MPa
• Flexural Strength: 90 MPa
• Elongation at Break: 2%
• Notched Izod Impact: 26.00 J/m
• Unnotched Izod impact strength: 90 J/m
• HDT at 0.45 MPa: 67 °C
• HDT at 1.82 MPa: 58 °C

• Store and use resins at room temperature, in dark, ventilated areas.
• Shake resin well before each use.
• Rinse method: Clean with alcohol spray and air gun, avoid immersion in alcohol for over 45 seconds.
• Store used resins in a closed, opaque bottle; avoid mixing used and new resins.
• Keep resins away from children and direct sunlight.
• Wear gloves and masks when handling resins; wash thoroughly if contact with skin or eyes occurs.
• Do not dispose of resin directly; cure it and treat it as regular plastic waste.
• Use Phrozen resins promptly after purchase, as unopened resins have a shelf life of one year.
• Post-process by letting prints dry for 30 minutes after washing, then cure for 120 minutes for optimal results.
• Minor color differences between printed parts and website images do not affect final performance.